API 5CT OCT K55 Casing Pipe Stainless Steel Standard Seamless Steel Price Pipe Heat Treatment Round Carbon Steel Spray Paint
QUALITY ASSURANCE :
- All products are produced by large factories
- Professional quality inspection tracking team
- Can accept any third party inspection
- Accept third party supervision
K55 API casing or Tubing is a relatively common one in Oil drilling. Because of the low steel grade of K55, it is used for shallow Oil and gas extraction. Due to its low price among other grades of steel, it enjoys broader applications. The J55 API casing or tubing is widely used in the extraction of natural gas and coalbed methane, and can be commonly found in shallow wells, geothermal wells, and water wells.
api 5CT k55 casing tubing Type of Casing：
- short round Thread casing(SC)
- long round thread casing(LC)
- buttress thread casing(BC)
API 5CT k55 casing Tubing mechanical properties:
| Tensile and Hardness Requirements | |||||||||
| Grade | Yield strength MPa | Tensile Strength | Hardness a,c | Specified wall thickness | Allowable Hardness Variation b | ||||
| Type | Total Elongation Under Load | min MPa | max | ||||||
| min | max | HRC | HBW | mm | HRC | ||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 |
| H40 | — | 0.5 | 276 | 552 | 414 | — | — | — | — |
| J55 | — | 0.5 | 379 | 552 | 517 | — | — | — | — |
| K55 | — | 0.5 | 379 | 552 | 655 | — | — | — | — |
| N80 | 1 | 0.5 | 552 | 758 | 689 | — | — | — | — |
| N80 | Q | 0.5 | 552 | 758 | 689 | — | — | — | — |
| R95 | — | 0.5 | 655 | 758 | 724 | — | — | — | — |
| L80 L80 | 1 | 0.5 | 552 | 655 | 655 | 23 | 241 | — | — |
| L80 | 9Cr 13Cr | 0.5 | 552 | 655 | 655 | 23 | 241 | — | — |
| 0.5 | 552 | 655 | 655 | 23 | 241 | — | — | ||
| C90 | 1 | 0.5 | 621 | 724 | 689 | 25.4 | 255 | £12.70 | 3 |
| 12.71 to 19.04 | 4 | ||||||||
| 19.05 to 25.39 | 5 | ||||||||
| ³ 25.40 | 6 | ||||||||
| T95 | 1 | 0.5 | 655 | 758 | 724 | 25.4 | 255 | £12.70 | 3 |
| 12.71 to 19.04 | 4 | ||||||||
| 19.05 to 25.39 | 5 | ||||||||
| ³ 25.40 | 6 | ||||||||
| C110 | — | 0.7 | 758 | 828 | 793 | 30 | 286 | £12.70 | 3 |
| 12.71 to 19.04 | 4 | ||||||||
| 19.05 to 25.39 | 5 | ||||||||
| ³ 25.40 | 6 | ||||||||
| P110 | — | 0.6 | 758 | 965 | 862 | — | — | — | — |
| Q125 | 1 | 0.65 | 862 | 1034 | 931 | b | — | £12.70 | 3 |
| 12.71 to 19.04 19.05 | 4 | ||||||||
| 5 | |||||||||
| a In case of dispute, laboratory Rockwell C hardness testing shall be used as the referee method. | |||||||||
| b No hardness limits are specified, but the maximum variation is restricted as a manufacturing control in accordance with 7.8 and 7.9. | |||||||||
| c For through-wall hardness tests of Grades L80 (all types), C90, T95 and C110, the requirements stated in HRC scale are for maximum mean hardness number. | |||||||||