The Benefits of Using Seamless steel Pipes in Various Industries
Seamless steel pipes have become an essential component in various industries due to their numerous benefits. These pipes are made from a solid piece of steel, without any seams or joints, which makes them highly durable and resistant to leaks. They are widely used in industries such as Oil and gas, construction, automotive, and manufacturing, among others. In this article, we will explore the benefits of using seamless steel pipes in these industries. One of the primary advantages of seamless steel pipes is their strength and durability. These pipes are manufactured using a process called extrusion, where a solid steel billet is heated and forced through a die to form the desired shape. This process ensures that the pipes have a consistent thickness and are free from any weak points or defects. As a result, seamless steel pipes can withstand high pressure and temperature, making them ideal for transporting fluids and gases in industries such as oil and gas.Tensile and Hardness Requirements | |||||||||
Grade | Yield strength MPa | Tensile Strength | Hardness a,c | Specified Wall thickness | Allowable Hardness Variation b | ||||
Type | Total Elongation Under Load | min MPa | max | ||||||
min | max | HRC | HBW | mm | HRC | ||||
1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 |
H40 | — | 0.5 | 276 | 552 | 414 | — | — | — | — |
J55 | — | 0.5 | 379 | 552 | 517 | — | — | — | — |
K55 | — | 0.5 | 379 | 552 | 655 | — | — | — | — |
N80 | 1 | 0.5 | 552 | 758 | 689 | — | — | — | — |
N80 | Q | 0.5 | 552 | 758 | 689 | — | — | — | — |
R95 | — | 0.5 | 655 | 758 | 724 | — | — | — | — |
L80 L80 | 1 | 0.5 | 552 | 655 | 655 | 23 | 241 | — | — |
L80 | 9Cr 13Cr | 0.5 | 552 | 655 | 655 | 23 | 241 | — | — |
0.5 | 552 | 655 | 655 | 23 | 241 | — | — | ||
C90 | 1 | 0.5 | 621 | 724 | 689 | 25.4 | 255 | £12.70 | 3 |
12.71 to 19.04 | 4 | ||||||||
19.05 to 25.39 | 5 | ||||||||
³ 25.40 | 6 | ||||||||
T95 | 1 | 0.5 | 655 | 758 | 724 | 25.4 | 255 | £12.70 | 3 |
12.71 to 19.04 | 4 | ||||||||
19.05 to 25.39 | 5 | ||||||||
³ 25.40 | 6 | ||||||||
C110 | — | 0.7 | 758 | 828 | 793 | 30 | 286 | £12.70 | 3 |
12.71 to 19.04 | 4 | ||||||||
19.05 to 25.39 | 5 | ||||||||
³ 25.40 | 6 | ||||||||
P110 | — | 0.6 | 758 | 965 | 862 | — | — | — | — |
Q125 | 1 | 0.65 | 862 | 1034 | 931 | b | — | £12.70 | 3 |
12.71 to 19.04 19.05 | 4 | ||||||||
5 | |||||||||
a In case of dispute, laboratory Rockwell C hardness testing shall be used as the referee method. | |||||||||
b No hardness limits are specified, but the maximum variation is restricted as a manufacturing control in accordance with 7.8 and 7.9. | |||||||||
c For through-wall hardness tests of Grades L80 (all types), C90, T95 and C110, the requirements stated in HRC scale are for maximum mean hardness number. |
Chemical Composition | C | Mn | P≤ | S≤ | Si≤ |
0.06-0.18 | 0.27-0.63 | 0.035 | 0.035 | 0.25 |
Labels | Outside diameter (d/mm) | T&C (kg/m) | Wall thickness (t/mm) | Type of end-finish | |||||||
1 | 2 | J55/K55 | M65 | L80/R95 | N80-1/Q | C90/T95 | P110 | Q125 | |||
4-1/2 | 9.50 | 114.30 | 14.14 | 5.21 | PS | PS | – | – | – | – | – |
10.50 | 114.30 | 15.63 | 5.69 | PSB | PSB | – | – | – | – | – | |
11.60 | 114.30 | 17.26 | 6.35 | PSLB | PLB | PLB | PLB | PLB | PLB | – | |
13.50 | 114.30 | 20.09 | 7.37 | – | PLB | PLB | PLB | PLB | PLB | – | |
15.10 | 114.30 | 22.47 | 8.56 | – | – | – | – | – | PLB | PLB | |
5 | 11.50 | 127.00 | 17.11 | 5.59 | PS | PS | – | – | – | – | – |
13.00 | 127.00 | 19.35 | 6.43 | PSLB | PSLB | – | – | – | – | – | |
15.00 | 127.00 | 22.32 | 7.52 | PSLB | PLB | SLB | PLB | PLB | PLB | ||
18.00 | 127.00 | 26.79 | 9.19 | – | PLB | SLB | PLB | PLB | PLB | PLB | |
21.40 | 127.00 | 31.85 | 11.10 | – | PLB | PLB | PLB | PLB | PLB | PLB | |
23.20 | 127.00 | 34.53 | 12.14 | – | – | PLB | PLB | PLB | PLB | PLB | |
24.10 | 127.00 | 35.87 | 12.70 | – | – | PLB | PLB | PLB | PLB | PLB | |
5-1/2 | 14.00 | 139.70 | 20.83 | 6.20 | PS | PS | – | – | – | – | – |
15.50 | 139.70 | 23.07 | 6.98 | PSLB | PSLB | – | – | – | – | – | |
17.00 | 139.70 | 25.30 | 7.72 | PSLB | PLB | PLB | PLB | PLB | PLB | – | |
20.00 | 139.70 | 29.76 | 9.17 | – | PLB | PLB | PLB | PLB | PLB | – | |
23.00 | 139.70 | 34.23 | 10.54 | – | PLB | PLB | PLB | PLB | PLB | PLB | |
26.80 | 139.70 | 39.88 | 12.70 | – | – | – | – | P | – | – | |
29.70 | 139.70 | 44.20 | 14.27 | – | – | – | – | P | – | – | |
32.60 | 139.70 | 48.52 | 15.88 | – | – | – | – | P | – | – | |
35.30 | 139.70 | 52.53 | 17.45 | – | – | – | – | P | – | – | |
38.00 | 139.70 | 56.55 | 19.05 | – | – | – | – | P | – | – | |
40.50 | 139.70 | 60.27 | 20.62 | – | – | – | – | P | – | – | |
43.10 | 139.70 | 64.14 | 22.22 | – | – | – | – | P | – | – | |
6-5/8 | 20.00 | 168.28 | 29.76 | 7.32 | PSLB | PSLB | – | – | – | – | – |
24.00 | 168.28 | 35.72 | 8.94 | PSLB | PLB | PLB | PLB | PLB | PLB | – | |
28.00 | 168.28 | 41.67 | 10.59 | – | PLB | PLB | PLB | PLB | PLB | – | |
32.00 | 168.28 | 47.62 | 12.06 | – | – | PLB | PLB | PLB | PLB | PLB | |
7 | 17.00 | 177.80 | 25.30 | 5.87 | – | – | – | – | – | – | – |
20.00 | 177.80 | 29.76 | 6.91 | PS | PS | – | – | – | – | – | |
23.00 | 177.80 | 34.23 | 8.05 | PSLB | PLB | PLB | PLB | PLB | – | – | |
26.00 | 177.80 | 38.69 | 9.19 | – | PLB | PLB | PLB | PLB | PLB | – | |
29.00 | 177.80 | 43.16 | 10.36 | – | PLB | PLB | PLB | PLB | PLB | – | |
32.00 | 177.80 | 47.62 | 11.51 | – | PLB | PLB | PLB | PLB | PLB | – | |
35.00 | 177.80 | 52.09 | 12.65 | – | – | PLB | PLB | PLB | PLB | PLB | |
38.00 | 177.80 | 56.55 | 13.72 | – | – | PLB | PLB | PLB | PLB | PLB | |
42.70 | 177.80 | 63.55 | 15.88 | – | – | – | – | P | – | – | |
46.40 | 177.80 | 69.05 | 17.45 | – | – | – | – | P | – | – | |
50.10 | 177.80 | 74.56 | 19.05 | – | – | – | – | P | – | – | |
53.60 | 177.80 | 79.77 | 20.62 | – | – | – | – | P | – | – | |
57.10 | 177.80 | 84.98 | 22.22 | – | – | – | – | P | – | – | |
7-5/8 | 24.00 | 193.68 | 35.72 | 7.62 | – | – | – | – | – | – | |
26.40 | 193.68 | 39.29 | 8.33 | PSLB | PSLB | PLB | PLB | PLB | – | – | |
29.70 | 193.68 | 44.20 | 9.52 | – | PLB | PLB | PLB | PLB | PLB | – | |
33.70 | 193.68 | 50.15 | 10.92 | – | PLB | PLB | PLB | PLB | PLB | – | |
39.00 | 193.68 | 58.04 | 12.70 | – | – | PLB | PLB | PLB | PLB | PLB | |
42.80 | 193.68 | 63.69 | 14.27 | – | – | PLB | PLB | PLB | PLB | PLB | |
45.30 | 193.68 | 67.42 | 15.11 | – | – | PLB | PLB | PLB | PLB | PLB | |
47.10 | 193.68 | 70.09 | 15.88 | – | – | PLB | PLB | PLB | PLB | PLB | |
51.20 | 193.68 | 76.20 | 17.45 | – | – | – | – | P | – | – | |
55.30 | 193.68 | 82.30 | 19.05 | – | – | – | – | P | – | – | |
7-3/4 | 46.10 | 196.85 | 68.61 | 15.11 | – | – | P | P | P | P | P |
8-5/8 | 24.00 | 219.08 | 35.72 | 6.71 | PS | PS | – | – | – | – | – |
28.00 | 219.08 | 41.67 | 7.72 | PS | – | – | – | – | – | ||
32.00 | 219.08 | 47.62 | 8.94 | PSLB | PSLB | – | – | – | – | – | |
36.00 | 219.08 | 53.58 | 10.16 | PSLB | PSLB | PLB | PLB | PLB | PLB | – | |
40.00 | 219.08 | 59.53 | 11.43 | – | PLB | PLB | PLB | PLB | PLB | – | |
44.00 | 219.08 | 65.48 | 12.70 | – | – | PLB | PLB | PLB | PLB | – | |
49.00 | 219.08 | 72.92 | 14.15 | – | – | PLB | PLB | PLB | PLB | PLB | |
9-5/8 | 32.30 | 244.48 | 48.07 | 7.92 | – | – | – | – | – | – | – |
36.00 | 244.48 | 53.58 | 8.94 | PSLB | PSLB | – | – | – | – | – | |
40.00 | 244.48 | 59.53 | 10.03 | PSLB | PSLB | PLB | PLB | PLB | – | – | |
43.50 | 244.48 | 64.74 | 11.05 | – | PLB | PLB | PLB | PLB | PLB | – | |
47.00 | 244.48 | 69.95 | 11.99 | – | PLB | PLB | PLB | PLB | PLB | PLB | |
53.50 | 244.48 | 79.62 | 13.84 | – | – | PLB | PLB | PLB | PLB | PLB | |
58.40 | 244.48 | 86.91 | 15.11 | – | – | PLB | PLB | PLB | PLB | PLB | |
59.40 | 244.48 | 88.40 | 15.47 | – | – | – | – | P | – | – | |
64.90 | 244.48 | 96.58 | 17.07 | – | – | – | – | P | – | – | |
70.30 | 244.48 | 104.62 | 18.64 | – | – | – | – | P | – | – | |
75.60 | 244.48 | 112.51 | 20.24 | – | – | – | – | P | – | – | |
10-3/4 | 32.75 | 273.05 | 48.74 | 7.09 | – | – | – | – | – | – | – |
40.50 | 273.05 | 60.27 | 8.89 | PSB | PSB | – | – | – | – | – | |
45.50 | 273.05 | 67.71 | 10.16 | PSB | PSB | – | – | – | – | – | |
51.00 | 273.05 | 75.90 | 11.43 | PSB | PSB | PSB | PSB | PSB | PSB | – | |
55.50 | 273.05 | 82.60 | 12.57 | – | PSB | PSB | PSB | PSB | PSB | – | |
60.70 | 273.05 | 90.33 | 13.84 | – | – | – | – | PSB | PSB | PSB | |
65.70 | 273.05 | 97.77 | 15.11 | – | – | – | – | PSB | PSB | PSB | |
73.20 | 273.05 | 108.94 | 17.07 | – | – | – | – | P | – | – | |
79.20 | 273.05 | 117.87 | 18.64 | – | – | – | – | P | – | – | |
85.30 | 273.05 | 126.94 | 20.24 | – | – | – | – | P | – | – | |
11-3/4 | 42.00 | 298.45 | 62.50 | 8.46 | – | – | – | – | – | – | – |
47.00 | 298.45 | 69.95 | 9.53 | PSB | PSB | – | – | – | – | – | |
54.00 | 298.45 | 80.36 | 11.05 | PSB | PSB | – | – | – | – | – | |
60.00 | 298.45 | 89.29 | 12.42 | PSB | PSB | PSB | PSB | PSB | PSB | PSB | |
65.00 | 298.45 | 96.73 | 13.56 | – | – | P | P | P | P | P | |
71.00 | 298.45 | 105.66 | 14.78 | – | – | P | P | P | P | P | |
13-3/8 | 48.00 | 339.72 | 71.43 | 8.38 | – | – | – | – | – | – | – |
54.50 | 339.72 | 81.11 | 9.65 | PSB | PSB | – | – | – | – | – | |
61.00 | 339.72 | 90.78 | 10.92 | PSB | PSB | – | – | – | – | – | |
68.00 | 339.72 | 101.20 | 12.19 | PSB | PSB | PSB | PSB | PSB | PSB | – | |
72.00 | 339.72 | 107.15 | 13.06 | – | – | PSB | PSB | PSB | PSB | PSB | |
16 | 65.00 | 406.40 | 96.73 | 9.53 | – | – | – | – | – | – | – |
75.00 | 406.40 | 111.62 | 11.13 | PSB | PSB | – | – | – | – | – | |
84.00 | 406.40 | 125.01 | 12.57 | PSB | PSB | – | – | – | – | – | |
109.00 | 406.40 | 162.21 | 16.66 | P | – | P | P | – | P | P | |
18-5/8 | 87.50 | 473.08 | 130.22 | 11.05 | PSB | PSB | – | – | – | – | – |
20 | 94.00 | 508.00 | 139.89 | 11.13 | PSLB | PSLB | – | – | – | – | – |
106.50 | 508.00 | 158.49 | 12.70 | PSLB | PSLB | – | – | – | – | – | |
133.00 | 508.00 | 197.93 | 16.13 | PSLB | – | – | – | – | – | – |